EOS NickelAlloy IN718

Product Summary

Suitable for
EOS M 290 @ 20 & 40 µm,
EOS M 400 @ 40 µm, EOS M 300-4 @ 40 µm, EOS M 400-4 @ 40 µm

High tensile, fatigue, creep and rupture strength at temperatures unto 700 °C

Item No 9011-0020
Shipping 3-4 business days
Contact sales team

EOS NickelAlloy IN718 is a precipitation-hardening nickel-chromium alloy that is characterized by having good tensile, fatigue, creep and rupture strength at temperatures up to 700 °C (1.290 °F). Parts built from EOS NickelAlloy IN718 can be easily post-hardened by precipitation- hardening heat treatments. In both as-built and age-hardened states the parts can be machined, spark eroded, welded, micro shot-peened, polished and coated if required.  The material is ideal for many high temperature applications such as gas turbine parts, instrumentation parts, power and process industry parts etc. It also has excellent potential for cryogenic applications. Due to the layerwise building method, the parts have certain anisotropy.
.

Part design by Ariane Group Injector Head Component, made of EOS NickelAlloy 718

The chemical composition in compliance with UNS N07718, AMS 5662, AMS 5664, 2.4668, NiCr19Fe19NbMo3
Ultimate Tensile Strength 1020 MPa
Yield Strength 710 MPa
Elongation @ Break 29 %

→ Instrumentation parts

→ Power industry parts

→ Process industry parts
→ Load-bearing components for high temperature applications up to 700 °C, good potential for cryogenic applications

→ Gas turbine components 

Product Summary

Suitable for
EOS M 290 @ 20 & 40 µm,
EOS M 400 @ 40 µm, EOS M 300-4 @ 40 µm, EOS M 400-4 @ 40 µm

High tensile, fatigue, creep and rupture strength at temperatures unto 700 °C

Item No 9011-0020
Shipping 3-4 business days
Contact sales team